Toughened Glass

Hopson Glass Group Co., Ltd | Updated: Jun 17, 2017
Source:

Basic Info

  • Model NO.: safety glass

  • Appearance: Flat Tempered

  • Steel Degree: Tempered Glass

  • Thickness of Curve Tempered Glass: 10MM

  • Technics: Physically Tempered

  • Usage: Building, Furniture, Home Appliance

  • Colored: Grey Bronze Clear Frosted

  • Shape: Flat

  • Standard: GB/T 9963-1998

  • Thickness of Flat Tempered Glass: 12MM

  • Fragment State: Ⅱ

  • Flatness: Conforming Article

  • Thickness: 2mm-19mm

Product Description

Tempered and Heat Strengthened Glass
Tempered and heat-strengthened glass is made by heating ordinary glass to its softening point and then suddenly cooling down to form compression in the surface layer of the glass, thus the mechanical strength is increased by times.

Features of Tempered Glass
Safety: Once breakage occurs, the glass disintegrates into small cubical fragments which are relatively harmless to human body.
High strength: 5 times stronger than annealed glass.
Excellent thermal stability: it withstands abrupt change of temperature.

Features of Heat Strengthened Glass
Mechanical strength is 1.6-2 times of annealed glass. 
Outstanding thermal stability.
Flatness is close to annealed glass and much better than tempered glass

Applications
- Window and door                                    
- Facades and curtain walls               
- Automobile,train,vessel                    
- Furniture and decoration

Specifications
Thickness:3~19mm
Max. size: 144"X355",  98"X504"
(3660X9000mm, 2500X12800mm)

Quality Standards
GB 15763.2, Chinese standard.
EN 12150.1, European standard.
EN 12600,  European standard.
ANSI Z97.1,  American standard.
AS/NZS 2208, Australian standard.

Heat Soak Test
Heat soak testing is a three-stage process that includes a ramp-up, dwelling time at 290oC and a cool-down phase. Heat soak testing is performed on fully tempered uncoated or pyrolytic glass products to reduce the probability of spontaneous breakage due to nickel sulfide inclusions that may exist in tempered float glass.

Applications
All tempered glass should undergo heat soak test.

Specifications
Thickness: 3~19mm
Max. Size: 98"X236", (2500X6000mm)

Quality Standards
GB 15763.4, Chinese standard.
EN 14179.1, European Standard.

Bent Tempered Glass and Curved Tempered Glass
Bent Tempered Glass and Curved Tempered Glass adopt the similar process with tempered glass, but before the cooling process, using the external power bent the glass to a proper radian according to the requirement, its wind pressure resistance is better than flat tempered glass and other kinds of glass for the special shape. It widely use in esthetics architecture field for the beautiful appearance.

Applications
- Facades and curtain walls
- External walls of revolving doors and exposed elevators
- Stairs, handrails, skylights
- Partions, display shelves and furniture

Specifications
Thickness: 4~19mm
Min. Size:  9"X17", (220X430mm)
Max. Size: 96"X165", (2440X4200mm)
Curve depth: up to 500mm
Bending angle: up to 90"


Feedback
Hopson Glass Group Co., Ltd

If you are interested in our products ,please feel free to contact with us 